    您所在的位置:網站首頁 > > 產品中心 > 通用PVC材料 > PVC特種料環保型聚氯乙烯透明料 W-70(C) W-90(C)
    環保型聚氯乙烯透明料 W-70(C) W-90(C)
    Lead-free PVC Transparent Compound...
    型號:0

    參考價:¥

    說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
    Product Description產品描述
    Lead-freePVC transparent compound are granule compounds which are manufactured with mixing, plasticizing and pelletizing process. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
    環保型聚氯乙烯透明料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
     
    Characteristics and Application 特點及用途
    The products have excellent transparent properties, mechanical and physical properties and good processability. They can meet RoHS Standard. They are mainly used for the wire and cables and other materials which have transparent property requirements.
    產品具有良好的透明性和機械物理性能,加工性能優異,符合RoHS環保標準。主要用于有透明要求的材料。
     
    Processing Indicator加工工藝
    Recommend to use single-screw extruders with L/D= 20-25.
    建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
    Model
    牌號
    Machine Barrel Temperature
    機筒溫度
    Molding Temperature
    機頭溫度
    W-70(C) / W-90(C) 140-165℃ 165-175℃
     

    Physical and Electrical Properties
    機械物理性能及電性能指標

    Item

    試驗項目

    Unit
    單位
    Technical Requirements
    技術要求
    W-70(CJ) W-70(CH) W-90(CJ) W-90(CH)
    Tensile Strength
    拉伸強度
    MPa ≥15.0 ≥12.5 ≥15.0 ≥12.5
    Elongation at Break
    斷裂伸長率
    % ≥150 ≥200 ≥150 ≥200
    20℃Volume Resistivity
    20℃時體積電阻率
    Ω.m ≥1×1011 ≥1×108 ≥1×1011 ≥1×108
    200 Thermal Stability
    200℃時熱穩定時間
    min ≥50 ≥50 ≥50 ≥50
    Brittle Temperature with Impact
    沖擊脆化溫度
    -20±5 -35±5 -20±5 -35±5
    Hardness
    硬度
    Shore A 85±5 75±5 85±5 75±5
    Thermal Aging
    熱老化試驗
    \ 100℃×168h 100℃×168h 100℃×240h 100℃×240h
    Tensile Strength Variation
    拉伸強度變化率
    % ±30 ±30 ±30 ±30
    Elongation Variation
    斷裂伸長率變化率
    % ±30 ±30 ±30 ±30